PC
● Iarratas
A úsáidtear den chuid is mó i bhfón póca, i ríomhaire tionsclaíoch, i bhfeithicil leictreonach, agus i scannán scaoilte OCA.
● Sraith Táirgí
1. Scannán Bonn Scaoilte OCA - Sraith GM60, Sraith SFP
| Airíonna | Aonad | Sraith GM60/SFP | Gm60a | Gm60b | |||||||
| Tiús | μm | 50 | 75 | 100 bliain d'aois | 50 | 75 | 100 bliain d'aois | 50 | 75 | 100 bliain d'aois | |
| Neart teanntachta | MD | MPA | 203 | 214 | 180 | 226 | 194 | 210 | 226 | 184 | 210 |
| TD | MPA | 239 | 240 | 247 | 251 | 235 | 205 | 251 | 235 | 205 | |
| Fadú a bhriseadh | MD | % | 126 | 135 | 151 | 178 | 145 | 152 | 178 | 145 | 152 |
| TD | % | 105 | 124 | 121 | 140 | 122 | 136 | 140 | 122 | 136 | |
| Crapadh (150 ℃/30min) | MD | % | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 |
| TD | % | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
| Tarchur | % | 90.2 | 90.1 | 90.1 | 90.1 | 90.0 | 89.2 | 90.1 | 90.0 | 89.2 | |
| Admhaigh | % | 3.3 | 3.5 | 4.0 | 5.4 | 5.8 | 6.0 | 3.5 | 3.8 | 4.0 | |
2. Scannán Primer Antistatic - Sraith YM30
| Airíonna | Aonad | Ym30 | Ym30a | Ym30b | ||||
| Tiús | μm | 38 | 50 | 75 | 38 | 50 | 50 | |
| Crapadh (150 ℃/30min) | MD | % | 1.3 | 1.2 | 1.1 | 1.3 | 1.2 | 1.3 |
| TD | % | 0.04 | 0.01 | 0.02 | 0.03 | -0.01 | -0.01 | |
| Tarchur | % | 90.4 | 90.5 | 90.5 | 93.8 | 92.8 | 90.5 | |
| Admhaigh | % | 1.89 | 1.94 | 2.35 | 1.97 | 2.4 | 1.94 | |
| Friotaíocht dromchla | Ω | 105-7 | 108-10 | 105-7 | ||||
| Dath dromchla | Faoi bhrón | Taobh easnamh | DUSH DUBH | |||||
3. Scannán Bonn Oligomer Íseal - GM30/GM31/YM40
| Airíonna | Aonad | Gm30 | Gm31 | Ym40 | ||||
| Tiús | μm | 50 | 125 | 50 | 125 | 50 | 125 | |
| Crapadh (150 ℃/30min) | MD | % | 0.7 | 0.5 | 0.5 | 1.1 | 1.2 | 1.2 |
| TD | % | 0.2 | 0.2 | 0.4 | 0.9 | 0.04 | 0.01 | |
| Tarchur | % | 90.2 | 90.3 | 90.2 | 90.1 | 90.2 | 90.3 | |
| Admhaigh | % | 1.6 | 1.8 | 2.4 | 3.4 | 2.02 | 2.68 | |
| Soiléireacht | % | 99.4 | 99.3 | 97.6 | 94.6 | / | / | |